Color
|
N/A
|
-
|
Black
|
|
No Silicone
|
N/A
|
-
|
Silicone Free
|
|
Density
|
ASTM D297-13
|
g/cm3
|
0.9 - 1.3
|
|
Hardness
|
ASTM D2240-05
|
A scale
|
75-85
|
|
Ultimate Elongation with Grain Min.
|
ASTM D412-06a
|
%
|
15
|
|
Ultimate Elongation across Grain Min.
|
ASTM D412-06a
|
%
|
40
|
|
Tensile Strength with Grain Min.
|
ASTM D412-06a
|
MPa (psi)
|
5.2 (754)
|
|
Tensile Strength across Grain Min.
|
ASTM D412-06a
|
MPa (psi)
|
3 (437)
|
|
Tear Strength Die B with Grain Min.
|
ASTM D624-00
|
kN/m (lbf/in)
|
26.25 (150)
|
|
Tear Strength Die B across Grain Min.
|
ASTM D624-00
|
kN/m (lbf/in)
|
52.50 (300)
|
|
Abrasion Resistance 1000 Cycle w/ CS17 Wheel Max.
|
ASTM D4060-10
|
mg
|
120
|
|
Low Temperature Brittleness |
ASTM D2137-11
Method C
|
- |
Non - Brittle in Both Directions @ -40°C |
|
Flammability - Maximum Burn Rate 100 mm/min |
FMVSS 302 |
mm/min |
100 Max. |
|
Ozone Resistance Tear Die B exposed 50 hrs @ 100 pphm @ 38°C then pulled @ 20 in/mm (Min.) |
|
Tear - with Grain
|
ASTM D1149-12
|
kN/m (lbf/in)
|
26.25 (150)
|
|
Tear - against Grain
|
ASTM D1149-12
|
kN/m (lbf/in)
|
26.25 (150)
|
|
No Cracks using 7x Magnification
|
ASTM D1149-12
|
kN/m (lbf/in)
|
No Cracks
|
|
Heat Aged Properties - Specimens Aged 70 hours @ 70°C (158°F) in Forced Air Oven |
|
Hardness % Shore A Pts Max.
|
ASTM D573-04
|
%
|
+/-10
|
|
Ultimate Elongation with Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Ultimate Elongation across Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Tensile Strength Ultimate with Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Tensile Strength Ultimate across Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Tear Resistance with Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Tear Resistance across Grain Max.
|
ASTM D573-04
|
%
|
+/-25
|
|
Surface Condition
|
-
|
-
|
Non-Brittle in Both Directions
|